| TPX MX002 三井化学株式会社 物性数据 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 其它性能 | 吸水率（24hr） | --- | ASTM D-570 | 0.01 | % |
| 物理性能 | 密度 | --- | ASTM D-1505 | 0.835 | g/cm3 |
| 熔点 | --- | MCI方法 | 222 | ℃ | |
| 熔融指数（260℃,5kg） | --- | ASTM D-1238 | 21 | g/10min | |
| 机械性能 | 屈服拉伸强度 | --- | ASTM D-638 | 25 | MPa |
| 拉伸模量 | --- | ASTM D-638 | 785 | MPa | |
| 拉伸强度 | --- | ASTM D-638 | 18 | MPa | |
| 断裂伸长率 | --- | ASTM D-638 | 60 | % | |
| 弹性强度 | --- | ASTM D-790 | 25 | MPa | |
| 弹性模量 | --- | ASTM D-790 | 640 | MPa | |
| Izod耐冲击强度 | --- | ASTM D-256 | 98 | KJ/m2 | |
| Rockwell硬度 | --- | ASTM D-785 | R62 | --- | |
| 电气性能 | 介电消散因子（23℃,1MHz） | --- | ASTM D-150 | 0.016 | --- |
| 体积电阻系数 | --- | ASTM D-257 | >1016 | Ωcm | |
| 介电强度 | --- | ASTM D-149 | 63 | KV/mm | |
| 介电常数（100～1MHz） | --- | ASTM D-150 | 2.12 | --- | |
| 热 性 能 | 模收缩率（纵向/横向） | --- | MCI方法 | 1.6/1.6 | % |
| 线形膨胀系数 | --- | ASTM D-696 | 1.17*10-4 | 1/℃ | |
| 热传导系数 | --- | ASTM BS-847A | 4*10-4 | calcm/seccm2℃ | |
| 比热 | --- | ASTM C-351 | 0.47 | cal/g℃ | |
| 燃烧速率 | --- | ASTM D-635 | 2.54 | cm/min | |
| Vicat软化点 | --- | ASTM D-1525 | 151 | ℃ | |
| 热变形温度（4.6kg/cm2） | --- | ASTM D-648 | 75 | ℃ | |
| 其它性能 | 模糊度 | --- | ASTM D-1746 | 0.9 | % |
| 折射率 | --- | ASTM D-542 | 1.463 | nd | |
| 透光率 | --- | ASTM D-1746 | 93 | % | |