HLG5/HLGA3 单面硬化PC，用于防弹防砸玻璃等，尺寸2000mm*2920mm，厚度1.5mm-6mm，昆山陆家现货供应，

联系电话：13651945149

Lexan Margard HLG5 sheet is a transparent 1-side hard coated lamination grade offering excellent optical properties for lamination with
glass in mainly asymmetrical bullet resistant security glazing panels. It can be specified to match specific levels of threat and has excellent
optical clarity. For cleaning instructions consult guidelines. Do not use abrasive or highly alkaline cleaners, never scrape the sheet with
squeegees, razor blades or other sharp instruments. Do not clean Lexan Margard HLG5 sheet in hot sun or at elevated temperatures. For
removal of paints, marking pen, inks, lipstick, labels, stickers etc. the use of kerosene, naphtha or white spirit is generally effective.
Afterwards, a warm final wash should be made, using a mild soap solution and ending with a thorough rinsing with cold water.

Property Test Method Unit Value
Physical
Density ISO 1183 g/cm3 1.20
Water absorption, 24 hours ISO 62 % 10.0
Mechanical
Tensile stress, yield ISO 527 MPa 60
Tensile strength, break ISO 527 MPa 70
Tensile elongation, yield ISO 527 % 6
Tensile elongation, break ISO 527 % 120
Tensile modulus ISO 527 MPa 2300
Flexural strength, yield ISO 178 MPa 90
Flexural modulus ISO 178 MPa 2300
Hardness ISO 2039/1 MPa 95
Taber abrasion, CS-10F, 500 cycles, 500g ##) ASTM D 1044 % Haze 8
Thermal
Vicat Softening Temp, Rate B ISO 306 °C 145
HDT, 0.45 MPa ISO 75 °C 138
Thermal conductivity ASTM C 177 W/m°C 0.20
Coeff. of Linear Therm. Expansion DIN53752 m/m°C 7x10-5
Thermal Index UL 746B °C 100
Optical
Light transmission (clear 112) ASTM D 1003 % 84-90
Imperfections#) DIN 52305-A-AZ - Pass