| 材质 | 塑胶 | 产品类别 | 陶氏PC |
|---|---|---|---|
| 质量等级 | 优良 | 规格 | 耐热性、耐冲击 |
| 适用范围 | 生产电话插头、电器产品配件和电子产品外壳 | 功能 | 通用级 |
| 颜色 | 本色 |
| PC 301V-10 美国陶氏化学公司 物性数据 |
| 规格级别： | --- | 外观颜色： | --- |
| 用途概述： | 用途：生产电话插头、电器产品配件和电子产品外壳。 | ||
| 备注说明： | 特性：提供优越的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||||||||
| 基本性能 | 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 10 | g/10min | |||||||||
| 密度 | --- | ASTM D-792 | 1200 | kg/m3 | ||||||||||
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % | ||||||||||
| 平衡吸水率 | 23℃，相对湿度50% | ASTM D-570 | 0.32 | % | ||||||||||
| 物理性能 | 折射率 | --- | ASTM D-542 | 1.586 | --- | |||||||||
| 透光率 | --- | ASTM D-1003 | 89 | % | ||||||||||
| 雾度 | --- | ASTM D-1003 | 0.7-1.5 | % | ||||||||||
| 模具收缩率 | --- | ASTM D-955 | 0.005-0.007 | mm/mm | ||||||||||
| 机械性能 |
|
--- |
|
|
|
|||||||||
|
--- |
|
|
|
||||||||||
| 拉伸模量 | --- | ASTM D-638 | 2410 | MPa | ||||||||||
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | ||||||||||
| 弯曲模量 | --- | ASTM D-790 | 2410 | MPa | ||||||||||
| 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | J/m | ||||||||||
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | --- | ||||||||||
| 落锤冲击强度 | 总能量@23℃ | ASTM D-3763 | 87 | J | ||||||||||
| 洛氏硬度 | --- | ASTM D-785 | 73 | M标度 | ||||||||||
| 电气性能 | 辉光灯丝测试 | 2mm | IEC 695-2-1 | 850 | ℃ | |||||||||
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | V | ||||||||||
| 介电强度 | 60Hz | ASTM D-149 | 17 | kv/mm | ||||||||||
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | --- | ||||||||||
| 体积电阻率 | 23℃，干 | ASTM D-257 | 2.0×1017 | Ω.cm | ||||||||||
| 热 性 能 | 平均燃烧程度 | --- | ASTM D-635 | 25 | mm | |||||||||
| 球状压痕温度 | --- | IEC 598-1 | >125 | ℃ | ||||||||||
| 维卡软化点 | 50℃/hour | ASTM D-1525 | 149 | ℃ | ||||||||||
| 线性热收缩率 | @-40℃-82℃ | ASTM D-785 | 68×10-6 | mm/mm/℃ | ||||||||||
| 热变形温度 | 退火@0.45MPa(4mm) | ASTM D-648 | 144 | ℃ | ||||||||||
| 热变形温度 | 退火@1.82MPa(4mm) | ASTM D-648 | 141 | ℃ | ||||||||||
| 热变形温度 | 未退火@1.82MPa(4mm) | ASTM D-648 | 128 | ℃ | ||||||||||
| 其它性能 | 需氧系数 | --- | ASTM D-2863 | 26 | % | |||||||||