| PC 621-02 美国陶氏化学公司 物性数据 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 2.5 | G/10min |
| 密度 | --- | ASTM D-792 | 1200 | KG/m3 | |
| 吸水率 | 23℃，24hr | ASTM D-570 | 0.15 | % | |
| 吸水率 | 相对湿度50% | ASTM D-570 | 0.32 | % | |
| 物理性能 | 折射率 | --- | ASTM D-542 | 1.586 | --- |
| 透光率 | --- | ASTM D-1003 | 89 | % | |
| 雾度 | --- | ASTM D-1003 | 0.7-1.5 | % | |
| 模具收缩率 | --- | ASTM D-955 | 0.006-0.007 | mm/mm | |
| 机械性能 | 拉伸屈服强度 | --- | ASTM D-638 | 63 | MPa |
| 拉伸断裂强?? | --- | ASTM D-638 | 60 | MPa | |
| 屈服伸长率 | --- | ASTM D-638 | 6 | % | |
| 拉伸断裂伸长率 | --- | ASTM D-638 | 90 | % | |
| 拉伸模量 | --- | ASTM D-638 | 2270 | MPa | |
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | |
| 弯曲模量 | --- | ASTM D-790 | 2410 | MPa | |
| 缺口冲击强度 | 23℃ | ASTM D-256 | 930 | J/m | |
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | --- | |
| 热 性 能 | 热变形温度 | 退火@1.82MPa | ASTM D-648 | 137 | ℃ |
| 热变形温度 | 未退火@1.82MPa | ASTM D-648 | 128 | ℃ | |
| 维卡软化点 | 50℃/小时，50n重 | ASTM D-1525 | 146 | ℃ | |
| 线性热收缩率 | -40℃-82℃ | ASTM D-696 | 68×10-6 | ||